oxidation loss
英 [ˌɒksɪˈdeɪʃn lɒs]
美 [ˌɑːksɪˈdeɪʃn lɔːs]
网络 氧化损耗; 氧化烧损; 氧化損耗
双语例句
- Evaluation of the fired samples for oxidation percentage, weight loss, dense zone and microstructural characteristics of the zone is carried out.
对煅烧后的试样的氧化百分率、失重、致密层和致密层的显微结构特点作了鉴定。 - Moreover, the metal powder grader can avoid the oxidation, moisture absorption and agglomeration of powder and reduce loss.
而且还能避免粉体氧化、吸潮以及团聚，降低损耗。 - Research on oxidation kinetics model of coal based on carbon element loss rate
基于失碳速率的煤氧化动力学模型研究 - It can intensify a lot of properties of iron and steel in corrosion resistance, resistance to heat and oxidation resistance at high temperature, decrease the economic loss by corrosion and abrasion, prolong the life of ferrous products greatly and bring good benefits.
钢铁渗铝后可以增强其耐腐蚀、耐热及抗高温氧化等诸多性能从而大大的减少钢铁因锈蚀和磨损等造成的经济损失，延长钢铁件的使用寿命，提高经济效益。 - The discussion to reduce steel billet oxidation burning loss
减少钢坯氧化烧损的探讨 - The relationship between the oxidation weight loss and total weight loss of Carbon/ Carbon composites is found by the friction test of samples and the dynamometer test of the full scale carbon brakes of aircraft.
通过样品的摩擦试验和全尺寸飞机碳刹车装置的惯性动力试验，研究了碳/碳复合材料氧化重量损失与总的重量损失的关系。 - By measurement and analysis of combustion system and billet loss of oxidation in the heating furnace of hot rolling plant, the reasons for serious loss of oxidation are found out, and suitable measures are put forward in this paper.
通过对热轧厂两座加热炉的燃烧系统、氧化烧损进行的热工测试、分析，找出造成炉子氧化烧损严重的原因，并给出相应措施。 - The oxidation weight loss rate of binderless C/ C composite prepared by in situ carbonization of pre oxidized fibres ( PAN) was tested in the air, at 0.1 MPa, from 673 K to 973 K using thermo weight analysis method.
采用恒温热重法测定了在空气中，0.1MPa、673K到973K下预氧丝（即预氧化聚丙烯腈纤维）原位炭化无粘结剂C/C复合材料的氧化失重率； - As heating die sleeve, a few grain charcoal is added and oxygen is consumed by charcoal burning so that oxidation burning loss is reduced.
在加热模套时，可放入少量颗粒木炭，通过木炭的燃烧消耗氧气达到减少氧化烧损的目的。 - The XRD, SEM analysis, the oxidation weigh loss and annealing circulation experiment with the coating are done.
对涂层进行了XRD、SEM分析、氧化失重实验和热循环实验。 - According to different delay time, the proper strategies are presented by using minimum principle of optimal control theory, which can lower the fuel consumption and metal oxidation loss of a reheating furnace, and can increase metal quality.
根据不同待轧时间，运用最优控制理论中的最小值原理提出相应合理的待轧策略，以尽可能地减少待轧时加热炉的燃料消耗和钢坯的氧化烧损，提高产品的加热质量。 - As a result, the heating capacity and quality of heating furnace is improved, the slab surface oxidation burning loss is decreased and the gas consumption reduced and the economic benefit remarkable.
改造后使加热炉提高了加热能力和加热质量，减少了板坯表面氧化烧损，降低了煤气消耗，经济效益显著。 - Besides, the pectinase facilitated resveratrol extraction, the addition of SO2 avoided resveratrol oxidation, and the clarification of glutin caused the least loss of resveratrol.
果胶酶有利于白藜芦醇的浸出，SO2可防止白藜芦醇的氧化，明胶处理白藜芦醇损失最小。 - Heating time is shortened, oxidation burning loss is reduced, and production efficiency is raised when temperature is 1 000 ℃.
加热温度在1000℃时，可有效缩短加热时间、减少氧化烧损、提高生产效率； - The melting temperature is lower, which is bad for the display of flux, while the solubility of hydrogen is increased and the oxidation loss of the component is intensified if the melting temperature is higher, so the melting temperature will be appropriate;
熔炼温度过低，不利于熔剂作用的发挥。熔炼温度越高，氢的溶解度将随之增加，加剧了组元的氧化烧损，熔炼温度要适宜； - With well-suited amount of Si 3N 4 added, the oxidation loss rate of aluminum-carbon bricks can be decreased, and their anti-oxidation ability and corrosion resistance improved.
适当引入氮化硅，降低了铝炭砖的氧化失重率，提高了其抗脱磷剂侵蚀的能力及砖的抗氧化性能。 - In the same oxidation condition, the relative weight loss of gradient composite was 1/ 3 of C_f/ C composite.
同等氧化失重条件下，氧化相对质量损失是Cf/C复合材料的1/3。 - The brittleness of several V-Cr-Ti-Al-Si alloys caused by the pickup of oxygen and hydrogen in fusion reactor environments was studied by using a simulation method of high temperature oxidation and hydrogenation. The neutron irradiation induced ductility loss was also studied by using experimental data from references.
利用高温氧化和氢化等方法模拟在聚变堆环境中多种V-Cr-Ti-Al-Si合金因吸O和H而造成的脆性，并利用国外测试的V合金中子辐照后性能数据，分析了V合金的中子辐照脆性。 - Reasons of oxidation burning loss to heating furnace and its countermeasures
加热炉氧化烧损原因与对策分析 - Controlled cooling after rolling is widely used in high speed wire production line. Compared with natural cooling, it can not only improve cooling rate and reduce oxidation loss, but also guarantee the product quality.
高速线材的轧后控制冷却工艺，与轧后自然冷却相比，不仅可以提高冷却速度，减少氧化损耗，而且可以保证产品质量，因此得到广泛应用。 - This new process achieved zero production of nitrogen oxidation; it effectively reduced weight loss and pitting corrosion, and also achieved better smoothness and brightness. 3.
该工艺不但实现了氮氧化物的零排放，还能有效减缓物件失重、抑制点腐蚀，同时具有较好的整平和光亮效果。 - The wear rate of pin specimens without electric current shows a monotone increase with an increase in electric current. The wear mechanism is mainly attributed to adhesion and abrasion, oxidation and electric arc ablation loss.
有电流时，销试样的磨损率随电流的增加而增加，其摩擦面上有电弧烧蚀坑，同时伴有磨粒磨损，粘着磨损和氧化磨损。 - Under the same conditions, gain variation of the unit oxidation weight loss.
在同样的条件下，获得单位氧化失重量的变化规律。 - Samples were treated and detected with alkali-ash method and iodine content in Nang before and after baking of every group with arsenic-cerium oxidation reduction method, respectively. Statistics was taken to analyze the loss of iodine in Nangs of every section.
用碱示灰化法测定处理样品，砷-铈氧化还原法分别测定各组馕烤制前后碘元素含量，用卫生统计学分析各组馕中碘元素损失情况，对碘盐加工烤馕中碘含量损失的进行研究。 - The surface of piercing plug is modified so as to enhancing the surface hardness and wearing resistance and oxidation resistance in order to extend the plug service life and to reduce unnecessary loss.
因此，为了延长顶头的使用寿命，减少不必要的损耗，对顶头进行表面改性，从而提高其表面硬度、耐磨性及抗氧化性。 - The carbon element of sample with 4.94% Li2CO3 had the minimum oxidation loss, and the oxidation resistance of the coating was the best.
碳酸锂加入量为4.94%的试样C元素氧化损失最小，涂层抗氧化能力最强。